Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins
Published on: January 17, 2025
Effect of milling procedures in CAD-CAM systems on the color changes of CAD-CAM polymethyl methacrylate resin
Perihan Oyar1, Mutahhar Ulusoy2
1Department of Dental Prostheses Technology, Health Services Vocational High School, Hacettepe University, D Block, 3. Floor, Sihhiye, 06100, Ankara, Turkey. poyar73@gmail.com.
Purpose:
This study aimed to investigate the effects of new and used burs on CAD-CAM PMMA resin color changes following thermocycling.
Materials And Methods:
Twenty disk-shaped specimens (10 × 2 mm) were made using a single brand of CAD-CAM polymethyl methacrylate resin (Polident) for the color test. Group N consisted of half of the specimens that were machined using the new tungsten carbide bur set, and Group U consisted of the specimens that were milled using the used bur set (500 machining time). A color test was performed on the specimens both before and after thermocycling. For the statistical analysis, the Kruskal-Wallis and Dunn Pairwise Comparison tests were employed.
Results:
The ∆E* value of specimens (2.057) milled with the used bur was higher than those of specimens milled with the new bur (0.340), but this value is within clinically acceptable limits. After thermocycling, specimens milled with the utilized burs had the greatest L* (93.850) and b* (5.000) values. After thermocycling, statistically significant differences were discovered between Group N and Group U as well as between specimens milled with the utilized bur before and after thermocycling.
Conclusion:
Thermocycling process have an effect on the mean ∆E values of specimens milled with the used carbide bur, but these ∆E* values were not statistically significant.
Clinical Significance:
The color and clinical performance of CAD-CAM restorations may be affected by variations in CAD-CAM milling bur properties, particularly those related to their frequent use.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
08:29Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)
Published on: January 7, 2019