Chlorine-induced Gas-Solid coupled corrosion behaviors of tube materials in high steam parameter MSW incinerator

The fast development of the waste incineration industry requires deeper insights into heating surface corrosion behavior at higher operating parameters with complex corrosion sources. This research investigates the corrosion behaviors of three types of plates, namely SA210-C, TP310, and 12CrMoV, when subjected to simulated flue gas and fly ash deposition simultaneously at temperatures ranging from 500℃ to 620℃. The results indicate that the weight loss due to coupling corrosion was 2.5 to 84.5 times higher than that of gas-phase corrosion under the same operating conditions. Among the three stainless-steels, TP310 demonstrates superior corrosion resistance. It is worth noting that, under the gas-solid coupling corrosion conditions, we observed a distinct two-layer structure of corrosion products. Despite the fly ash simulants detaching over time, the two-layer structure remained unchanged. Based on the theory of eutectic molten salt formation, we propose that alkali metal chlorides only initiate the formation of the molten layer in the initial stage of corrosion. Furthermore, we offer additional suggestions for the mechanism of sustaining the molten layer in the absence of alkali metal chlorides.