Facile synthesis of a carbon supported lithium iron phosphate nanocomposite cathode material from metal-organic...

Lithium iron phosphate (LiFePO₄, LFP) has become one of the most widely used cathode materials for lithium-ion batteries. The inferior lithium-ion diffusion rate of LFP crystals always incurs poor rate capability and unsatisfactory low-temperature performances. To meet with the requirements from the ever-growing market, it is of great significance to synthesize carbon supported LFP nanocomposite (LFP/C) cathode materials using cost effective and environmentally friendly methods. In this work, an LFP/C cathode material is straightforwardly prepared from a metal-organic framework (MOF) precursor ferric gallate (Fe-GA) using its self-template effect. The Fe-GA precursor is firstly fabricated from the redox coprecipitation reaction between Fe foils and gallic acid (GA) molecules in mild aqueous phase. Then the Fe-GA is directly converted to the LFP/C sample after a following solid-state reaction. In half-cells, the LFP/C composite exhibits a reversible capacity of 109.7 mAh·g^-1 after 500 cycles under the current rate of 100 mA·g^-1 at 25 °C as well as good rate capabilities. In the LFP/C//graphite full-cells, the LFP/C composite can deliver a reversible capacity of 71.4 mAh·g^-1 after 50 cycles in the same condition as the half-cells. The electrochemical performances of the LFP/C cathode in half-cells at lower temperature of -10 °C are also examined. Particularly, the evolution of samples has been explored and the lithium-ion storage mechanism of the LFP/C cathode has been unveiled. The sample synthesis protocol is straightforward, eco-friendly and atomic efficient, which can be considered to have good potential for scaling-up.