Novel Use of Fractal Analysis for Quantifying Polymethylmethacrylate Distribution Patterns in Osteoporotic and...

Purpose: Fractal analysis is a mathematical tool which allows the evaluation of complex microstructural features within materials that cannot be expressed in traditional geometric terms. The purpose of this study is to quantify the differences in polymethylmethacrylate intravertebral cement spatial distribution patterns following vertebroplasty using fractal analysis through the examination of osteoporotic and malignant compression fractures. Methods: Frontal and lateral post-vertebroplasty radiographs were evaluated from 29 patients with osteoporotic and malignant compression fractures who underwent vertebroplasty. The individually treated vertebra were divided into osteoporotic (n = 35) and malignant groups (n = 41). Images underwent segmentation, thresholding, and binarization prior to fractal analysis. Fractal dimension and lacunarity values were derived from the region of interest in treated vertebrae using the "box-counting" and "gliding-box" techniques respectively using ImageJ. The mean values of both parameters were compared between the 2 groups. Results: The mean fractal dimension was significantly higher in the malignant vertebral compression fracture group (1.53 ± 0.08) compared to the osteoporotic group (1.34 ± 0.17; P < .001). Similarly, mean lacunarity values were significantly higher in the malignant fracture group (0.50 ± 0.09) compared to the osteoporotic group (0.37 ± 0.10; P < .001). Conclusions: Fractal dimension and lacunarity values of cement spatial distribution patterns obtained from the post-vertebroplasty radiographs can differentiate between benign osteoporotic and malignant vertebral compression fractures. This novel technique may be useful for evaluating cement spatial distribution patterns in spine augmentation procedures, although further research is warranted in this area.