Prodelphinidins enhance dentin matrix properties and promote adhesion to methacrylate resin

Investigate the bioactivity and stability of Rhodiola rosea (RR) fractions as a natural source of prodelphinidin gallate (PDg) on dentin collagen via analysis of the viscoelastic and resin-dentin adhesive properties of the dentin matrix.

The biomimicry and stability of RR subfractions (F1, F2, F3 and F4) with collagen were determined by dynamic mechanical analysis (DMA). DMA used a strain sweep method to assess the dentin matrix viscoelastic properties [storage (E'), loss (E"), and complex (E*) moduli and tan δ] after treatment, 7-, 30- and 90-days of storage in simulated body fluids (SBF). Resin-dentin interface properties were assessed after 1 and 90-days in SBF by microtensile bond strength test and confocal laser scanning microscopy. Data were analyzed using two and one-way ANOVA and post-hoc tests (α = 0.05).

RR fractions increased dentin matrix complex (96 - 69 MPa) and storage (95 - 68 MPa) moduli, compared to the control (∼9 MPa) in the ranking order: F2 ≥ F3 = F1 = F4 > control (p < 0.001). Treatment did not affect tan δ values. After 30- and 90-days, RR-treated dentin E*, E' and tan δ decreased (p < 0.001). F2 fraction yielded the highest microtensile bond strength (43.9 MPa), compared to F1, F4 (35.9 - 31.7 MPa), and control (29 MPa). RR-treated interfaces mediated stable surface modifications and enhanced collagen-methacrylate resin interactions at the bioadhesive interface.

Prodelphinidin gallates from RR are potent and reasonably stable biomimetic agents to dentin. Higher potency of F2 fraction with the dentin matrix and the adhesive interface is associated with a degree of polymerization of 2-3 and gallo(yl) motifs.