Interconnected Nanoporous Polysulfone by the Self-Assembly of Randomly Linked Copolymer Networks and Linear...

Porous materials have attracted considerable attention due to their versatile applications, especially in water purification. Interconnected nanoporous structures are distinguished by their high degree of porosity and resistance to clogging, as well as their insensitivity to nanostructural orientation. Previous works on randomly linked copolymer systems have shown that they can effectively produce disordered cocontinuous nanostructures, which upon removal of one component yield interconnected nanoporous materials. However, the cocontinuous nanomaterials previously developed using polystyrene (PS) and poly(d,l-lactic acid) (PLA) strands, and the resulting interconnected nanoporous PS monoliths, were far too brittle to enable practical use as membranes. Here, we study the self-assembly of randomly linked copolymer networks prepared using blocks of the engineering polymer polysulfone (PSU). A wide cocontinuous regime (spanning 40 wt %) was found for randomly end-linked copolymer networks (RECNs) constructed from PSU and PLA strands, via a combination of mechanical testing, gravimetry, small-angle X-ray scattering, and scanning electron microscopy. The PSU/PLA cocontinuous nanomaterial with symmetric composition showed 2.4 times higher Young's modulus and ∼100 times greater toughness than the corresponding PS/PLA sample. The interconnected nanoporous PSU fabricated after etching of PLA even exhibited 1.6 times greater toughness than PS/PLA prior to PLA removal. To facilitate the production of thin films of cocontinuous nanomaterials, we applied solution-processable randomly linked linear PSU/PLA multiblock polymers onto ultrafiltration membranes. The interconnected nanoporous PSU thin film generated by etching PLA was found to effectively reject 50 nm diameter particles without significantly compromising permeability. This discovery presents a valuable addition to the existing techniques used to fabricate PSU membranes. In contrast to traditional methods, which are sensitive to processing conditions, produce a wide range of pore sizes, and offer limited adjustability of pore size, the current technique is anticipated to enable interconnected PSU membranes with more uniform and tailorable porosity.