Exploring FAST Technique for Diffusion Bonding of Tungsten to EUROFERE97 in DEMO First Wall

The European Fusion Reactor (DEMO, Demonstration Power Plant) relies significantly on joining technologies in its design. Current research within the EUROfusion framework focuses on developing materials for the first wall and divertor applications, emphasizing the need for suitable joining processes, particularly for tungsten. The electric field-assisted sintering technique (FAST) emerges as a promising alternative due to its high current density, enabling rapid heating and cooling rates for fast sintering or joining. In this study, FAST was employed to join tungsten and EUROFERE97 steel, the chosen materials for the first wall, using 50-µm-thick Cu foils as interlayers. Three distinct joining conditions were tested at 980 °C for 2, 5, and 9 min at 41.97 MPa to optimize joint properties and assess FAST parameters influence. Hardness measurements revealed values around 450 HV_0.1 for tungsten, 100 HV_0.1 for copper, and 390 HV_0.1 for EUROFER97 under all joining conditions. Increasing bonding time improved joint continuity along the EUROFER97/Cu and W/Cu interfaces. Notably, the 5 min bonding time resulted in the highest shear strength, while the 9 min sample exhibited reduced strength, possibly due to Kirkendall porosity accumulation at the EUROFER97/Cu interface. This porosity facilitated crack initiation and propagation, diminishing interfacial adhesion properties.