Freeze-Thaw Cycle Durability and Mechanism Analysis of Zeolite Powder-Modified Recycled Concrete

The inferior mechanical performance and freeze-thaw (FT) resistance of recycled concrete are mostly due to the significant water absorption and porosity of recycled coarse particles. In this study, different dosages of zeolite powder were used in recycled concrete. A series of macroscopic tests were used to evaluate the workability and FT durability of zeolite powder-modified recycled concrete (ZPRC). X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to reveal the micro-mechanisms of FT resistance in ZPRC. The results show that the increase in zeolite powder content leads to a decrease in the slump and water absorption of ZPRC. Additionally, ZPRC with 10% zeolite powder has superior mechanical characteristics and tolerance to FT conditions. The higher strength and FT resistance of the ZPRC can be attributed to the particle-filling effect, water storage function, and pozzolanic reaction of zeolite powder, which results in a denser microstructure. The particle-filling effect of zeolite powder promotes the reduction of surface pores in recycled coarse aggregates (RCAs). The water storage function of zeolite powder can provide water for the secondary hydration of cement particles while reducing the free water content in ZPRC. The pozzolanic reaction of zeolite powder can also promote the generation of hydrated calcium silicate and anorthite, thereby making the microstructure of ZPRC more compact. These results provide theoretical guidance for the engineering application of recycled concrete in cold regions.