Effect of Bleaching Agents on Composite Resins with and without Bis-GMA: An In Vitro Study

The objective was to evaluate the change in color, hardness, and roughness produced by carbamide peroxide (CP) at two different concentrations on two resins. The 16% or 45% CP was applied to 66 resin discs with and without Bis-GMA. The color was measured with a spectrophotometer, and ΔE_ab and ΔE₀₀ were calculated. Microhardness tester and SEM were used. In both composites, the a* and b* coordinates tended to be red and yellow, respectively, and were significant in the Bis-GMA group (p < 0.05). The ΔE_ab and ΔE₀₀ were higher in the composite with Bis-GMA, regardless of the treatment received (p < 0.05). The microhardness was reduced in both composites regardless of the PC concentration compared to the control (p < 0.05). The 45% CP reduced the microhardness in the resin group with Bis-GMA compared to 16% CP (p < 0.001) but was not significant in the resin without Bis-GMA (p = 1). An increase in roughness was directly proportional to the concentration of CP, and it was more notable in the composite without Bis-GMA. The composite with Bis-GMA showed a greater tendency to darken than the one without Bis-GMA. The surface hardness of the composite was reduced in both composites and was not influenced by CP concentration in the composite without Bis-GMA. Bleaching is a common procedure nowadays. It is important to know how CP affects composites to establish a prognosis of the treatments in terms of color change, roughness, and hardness.