Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates
07:53

Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates

Published on: April 27, 2019

8.3K

Experimental Investigation into the Failure Mechanisms of Fabric Membrane Materials with Defective Flat Round Cracks

Wenrui Li1, Ping Liu1, Jiancheng Zhang1

  • 1School of Civil Engineering and Architecture, Jiangsu University of Science and Technology, Zhenjiang 212004, China.

Materials (Basel, Switzerland)
|June 27, 2024
PubMed

Keywords:
crack propagationfailure mechanismmembrane materialoblate initial crack

More Related Videos

Author Spotlight: Enhancing Fiber Composite Laminate Quality with the Wet Hand Lay-Up/Vacuum Bag Process09:54

Author Spotlight: Enhancing Fiber Composite Laminate Quality with the Wet Hand Lay-Up/Vacuum Bag Process

Published on: June 30, 2023

2.0K
Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method07:37

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method

Published on: January 16, 2019

9.7K

Related Concept Videos

Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
115
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
180
Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
2.3K
Types of Non-structural Cracks in Concrete01:28

Types of Non-structural Cracks in Concrete

Non-structural cracks are primarily of three types: plastic, early-age thermal, and drying shrinkage cracks. Plastic cracks are further classified into plastic shrinkage cracks and plastic settlement cracks.
Plastic shrinkage cracks typically form within hours after the concrete is poured. The concrete's surface dries faster than the bottom, creating tensile stress that the still-plastic concrete cannot withstand, leading to diagonal or randomly patterned cracks on the concrete surface.
141
Yield Criteria for Ductile Materials under Plane Stress01:25

Yield Criteria for Ductile Materials under Plane Stress

In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
The Maximum Shearing Stress Criterion, also known as...
159
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
153