Assessment of occlusion changes during laboratory phase of relining: An in vitro study
Ayush Verma1, D Krishna Prasad, Chethan Hegde
1Department of Prosthodontics and Crown and Bridge, A B Shetty Memorial Institute of Dental Sciences, NITTE (Deemed to be University), Mangalore, Karnataka, India.
Aim:
Assessment of occlusion changes during laboratory phase of relining is essential to evaluate the occlusal discrepancies that could get incorporated in the denture with the use of different relining materials. Since the long term stability and functional success of the denture is heavily influenced by occlusion, an In-vitro study to assess these changes after relining is warranted. The aim of the study is to evaluate the changes in occlusion during laboratory phase of relining procedure.
Settings And Design:
This is an in vitro study with a total of 30 specimen.
Materials And Methodology:
A total of 30 maxillary standardized dentures were fabricated after mounting on a semi adjustable articulator. These samples will be divided into three groups based on the relining material used (Autopolymerizing resin, Heat-cure resin, Tissue conditioner). The vertical dimension, Centric contact points and eccentric contact points were measured before and after relining.
Statistical Analysis Used:
The variables were tested to see if they had a normal distribution using the Shapiro-Wilk test. Parametric distribution was seen for ECP leading to further comparison using one way analysis of variance (ANOVA). Non-parametric distribution was found while testing the VD, CCP leading to adoption of Kruskal-wallis test for comparison of groups. Dunn Bonferroni test was done for VD since results were significant.
Results:
The results of this in-vitro study showed statistically significant difference with respect to change in vertical dimension in all groups pre and post relining (P = 0.005). The centric contact points showed lesser variation in position when comparing the pre to the post relining phase with the use of autopolymerising resins, whereas heat cure resins and tissue conditioners showed statistically significant difference in the centric point contacts post relining. No statistically significant changes were seen in eccentric occlusion post relining in all groups. Tissue conditioners showed minimum mean changes in eccentric contacts.
Conclusion:
Within the limitations of this study, the use of autopolymerising resins depicted the most stable results with respect to occlusion, for relining of dentures.