Demineralization activating highly-disordered lignite-derived hard carbon for fast sodium storage

Lignite, as one of the coal materials, has been considered a promising precursor for hard carbon anodes in sodium-ion batteries (SIBs) owing to its low cost and high carbon yield. Nevertheless, hard carbon directly derived from lignite pyrolysis typically exhibits highly ordered microstructure with narrow interlayer spacing and relatively unreactive interfacial properties, owing to the abundance of polycyclic aromatic hydrocarbons and inert aromatic rings within its molecular composition. Herein, an innovative demineralization activating strategy is established to simultaneously modulate the interfacial properties and the microstructure of lignite-derived carbon for the development of high-performance SIBs. Demineralization process not only creates numerous void spaces in the matrix of lignite precursor to assist aromatic hydrocarbon rearrangement, thereby reducing the ordering and expanding interlayer spacing, but also exposes more interfacial oxygen-containing functional groups to effectively increasing the sodium storage active sites. As a result, the optimal demineralized lignite-derived hard carbon (DLHC 1300) delivers a high reversible capacity of 335.6 mAh g^-1 at 30 mA g^-1, superior rate performance of 246.3 mAh g^-1 at 6 A g^-1 and nearly 100 % capacity retention after 1100 cycles at 1A g^-1. Furthermore, the optimized DLHC 1300 material functions as an outstanding anode in sodium ion full cells. This work significantly advances the development of low-cost, high-performance commercial hard carbon anodes for SIBs.