Controlling the Phase Distribution of Single Bromide Quasi-2-Dimensional Perovskite Crystals via Solvent Engineering...

To achieve pure-blue emission (460-470 nm), we manipulate the crystallization process of the quasi-2D perovskite, (PBA)₂CsPbBr₃, prepared by a solution process. The strategy involves controlling the distribution of "n" phases with different bandgaps, solely utilizing changes in the precursor's supersaturation to ensure that the desired emission aligns with the smallest bandgap. Adjustments in photoluminescence (PL) wavelength are made by changing the solute concentration and solvent polarity, as these factors heavily influence the diffusion of cations, a crucial determinant for the value of "n". Subsequently, we enhance the PL quantum yield from 31 to 51% at 461 nm using trioctylphosphine oxide (TOPO) as an additive of antisolvent, which passivates halide vacancy and promotes orderly crystal growth, leading to faster carrier transfer between phases. With these strategies, we successfully demonstrate pure-blue LEDs with a turn-on voltage of 3.3 V and an external quantum efficiency of 5.5% at an emission peak of 470 nm with a full-width at half-maximum of 31 nm.