Combined First-Principles and Experimental Investigation into the Reactivity of Codeposited Chromium-Carbon under...

High-pressure synthesis in the diamond anvil cell suffers from the lack of a general approach for the control of precursor stoichiometry and homogeneity. Here, we present results from a new method we have developed that uses magnetron cosputtering to prepare stoichiometrically precise and atomically mixed amorphous films of Cr:C. Laser-heated diamond anvil cell experiments carried out on a flake of this sample at pressures between 13.5 and 24.3 GPa lead to the observation of Cr₃C (Pnma) over the entire pressure range-in good agreement with our in-house theoretical predictions-but also reveal two other metastable phases that were not expected: a novel monoclinic chromium carbide phase and the NaCl-type CrC (Fm3̅m) phase. The unexpected stability of CrC is investigated by using first-principles methods, revealing a large stabilizing effect tied to substoichiometry at the carbon site. These results offer an important case study into the current limitations of crystal structure prediction methods with regard to phase complexity and bolster the growing need for advanced theoretical approaches that can more completely survey experimentally unexplored phase space.