Boosting piezoelectric properties of PVDF nanofibers via embedded graphene oxide nanosheets

Tremendous research efforts have been directed toward developing polymer-based piezoelectric nanogenerators (PENG) in a promising step to investigate self-charging powered systems (SCPSs) and consequently, support the need for flexible, intelligent, and ultra-compact wearable electronic devices. In our work, electrospun polyvinylidene fluoride (PVDF) nanofiber mats were investigated while graphene oxide (GO) was added with different concentrations (from 0 to 3 wt.%). Sonication treatment was introduced for 5 min to GO nanosheets before combined PVDF solution. A comprehensive study was conducted to examine the GO incremental effect. Microstructural and mechanical properties were examined using a scanning electron microscope (SEM) and a texture analyzer. Moreover, piezoelectric properties were assessed via various tests including impulse response, frequency effect, d₃₃ coefficient, charging and discharging analysis, and sawyer tower circuit. Experimental results indicate that incorporation of GO nanosheets enhances piezoelectric properties for all concentrations, which was linked to the increase in β phase inside the nanofibers, which has a significant potential of enhancing nanogenerator performance. PVDF-GO 1.5 wt.% shows a notably higher enhancing effect where the electroactive β-phase and γ-phase are recorded to be boosted to ~ 68.13%, as well as piezoelectric coefficient (d₃₃ ~ 55.57 pC/N). Furthermore, increasing impact force encouraged the output voltage. Also noted that the delivered open circuit voltage is ~ 3671 V/g and the power density is ~ 150 µw/cm². It was observed that GO of concentration 1.5 wt.% recorded a conversion efficiency of ~ 74.73%. All results are in line, showing better performance for PVDF-GO 1.5 wt.% for almost all concentrations.