Effect of BaTiO₃ Filler Modification with Multiwalled Carbon Nanotubes on Electric Properties of Polymer...

Two ranges of dielectric permittivity (k) increase in polymer composites upon the modification of BaTiO₃ filler with multiwalled carbon nanotubes (MWCNTs) are shown for the first time. The first increase in permittivity is observed at low MWCNT content in the composite (approximately 0.07 vol.%) without a considerable increase in dielectric loss tangent and electrical conductivity. This effect is determined by the intensification of filler-polymer interactions caused by the nanotubes, which introduce Brønsted acidic centers on the modified filler surface and thus promote interactions with the cyanoethyl ester of polyvinyl alcohol (CEPVA) polymer binder. Consequently, the structure of the composites becomes more uniform: the permittivity increase is accompanied by a decrease in the lacunarity (nonuniformity) of the structure and an increase in scale invariance, which characterizes the self-similarity of the composite structure. The permittivity of the composites in the first range follows a modified Lichtenecker equation, including the content of Brønsted acidic centers as a parameter. The second permittivity growth range features a drastic increase in the dielectric loss tangent and conductivity corresponding to the percolation effect with the threshold at 0.3 vol.% of MWCNTs.