Enhanced Flame-Retardant Properties of PVDF Using a Multiphase Synergistic Approach with Phytate-Chitosan-Modified...

The morphology and composition of inorganic particles play a vital role in controlling the flame-retardant characteristics of polymers. Halogen-free flame-retardant polymers have also become a current research hotspot. Boron nitride (BN), phytic acid (PA), and chitosan (CS), a natural polysaccharide with a nitrogen content of approximately 6.8-7.5%, show great promise as flame retardants owing to their high thermal stability, P-based flame retardancy, and natural polysaccharide properties, respectively. In this study, BN (BN@PA-CS) particles coated with PA and CS were designed and prepared via a facile modification strategy. The effect of BN@PA-CS on the mechanical and flame-retardant properties of polyvinylidene fluoride (PVDF) was further investigated, and it was found that both characteristics were improved. Compared to pure PVDF, the PVDF composite films exhibited a significantly lower peak heat release rate and total heat release. With a BN@PA-CS content of 20%, the peak was the lowest at 18.25 W/g, corresponding to a decrease of 77.83%. This phenomenon may be attributed to the synergistic effect of the BN nanosheets and PA-CS in the BN@PA-CS particles. This work describes a facile and effective method of modifying the morphology and composition of inorganic particles, thereby controlling the properties of polymers, and provides a new approach to improving the safety of PVDF battery separators.