Inline Hot Rolling of Al-5%Mg Strip Cast Using an Unequal Diameter Twin-Roll Caster

One advantage of twin-roll casting for aluminum alloys is that hot rolling can be omitted, thus shortening the process. The effect of inline hot rolling on the anisotropy of the mechanical properties, especially the elongation, of the roll-cast strip has not been investigated. In a high-speed twin-roll caster, inline hot rolling forms the metal shape before the temperature of the cast strip decreases below the temperature needed for hot rolling. In this study, inline hot rolling of Al-5%Mg strips cast using an unequal diameter twin-roll caster was performed to validate the technique and evaluate its ability to reduce surface cracking and improve the elongation anisotropy. A rolling speed of 30 m/min was used, and the effects of temperature and thickness reduction during inline hot rolling on the surface and mechanical properties were investigated. Inline hot rolling was found to effectively reduce the formation of surface cracks and the anisotropy of the mechanical properties.