Analysis of Thermoelastic Contact of Gas-Lubricated Rough Sealing Faces

Friction and wear are the main failure sources of face seals. When the surfaces of sealing rings exhibit greater roughness, the level of friction might increase and lead to sealing failure. Therefore, in this paper, based on the elastic contact hypothesis of rough and wavy surfaces and the influence of temperature on the elastic modulus of materials, a thermoelastic contact lubrication model of a gas-lubricated end seal is established. The novelty and advantage of this study is that it takes the effect of surface roughness into consideration during thermoelastic analysis of gas-lubricated seals. The film pressure, temperature, contact force and deformation of a gas spiral groove-faced seal are numerically determined. The influence of surface roughness on the contact distribution, deformation and temperature of the end-face seal at different speeds and pressures is analyzed. The film thickness increases as the rotational speed increases from 1 rpm to 2000 rpm, while the contact pressure sharply decreases from 0.25 kPa to 0. The analysis shows that the roughness contact mainly happens on the inner side of the rings due to convergent distortion of the seal faces, which easily causes partial wear of the seal faces. Moreover, it can also be found that the spiral grooves on the sealing surface can produce obvious hydrodynamic pressure effect due to the function of shear speed when the speed increases to 2000 rpm, while the film temperature increases from 293.3 K to about 306 K. The greater surface roughness results in a larger temperature rise under low-rotational-speed and lower-seal-pressure conditions, which further increases the risk of severe wear or even failure of the seal faces.