Investigation of the Compressive Strength and Void Analysis of Cement Pastes with Superabsorbent Polymer

This study aimed to experimentally investigate the compressive strength and air voids of cement pastes with varying dosages of Superabsorbent Polymer (SAP) and water-to-cement (w/c) ratios. Cement pastes were prepared using three different w/c ratios of 0.4, 0.5, and 0.6, along with different dosages of SAP ranging from 0.2% to 0.5% by weight of cement. Additionally, SAP was introduced in two forms: dry and wet. After casting the cubes, two distinct curing conditions were employed: curing at a temperature of 20 °C with a Relative Humidity (RH) of 60% (Curing 1), and water curing (Curing 2). The results revealed that the addition of SAP increased early strength when subjected to Curing 1, followed by a decrease in later strength. On the other hand, samples with SAP and water curing exhibited higher strength compared to those without SAP, especially with w/c ratios of 0.4 and 0.5. However, at a w/c ratio of 0.6, nearly all samples showed a reduction in strength compared to those without SAP. Furthermore, air void analysis was performed on all samples cured for 28 days using an image analysis technique. The samples containing wet SAP resulted in a higher total air content compared to the samples with dry SAP. Additionally, the incorporation of wet SAP in cement paste led to lower specific surface areas and a higher spacing factor than the samples with dry SAP. These findings suggest that the clumping of wet SAP particles during presoaking resulted in coarser air voids compared to the samples containing dry SAP.