Simultaneous Measurement of Two-Trace Two-Dimensional (2T2D) Near-Infrared (NIR) Asynchronous Correlation Spectra and...

In this study, a new system was developed to carry out simultaneous near-infrared (NIR) and small-angle X-ray scattering (SAXS) measurements. Aged polypropylene (PP) was examined with the NIR-SAXS system to demonstrate how it can be utilized to derive pertinent information about the polymer structure. Pairs of SAXS profiles and NIR spectra of PP in its initial state and after aging were measured to derive an in-depth understanding of the aging phenomenon. The SAXS profiles of the PP samples showed a clear shift of the SAXS peak to the lower q direction induced by the thermal aging, indicating an increase in the length of the long-period structure. Two-trace two-dimensional (2T2D) asynchronous correlation spectra derived from NIR spectra clearly revealed that the aging treatment leads to a substantial increase in the spectral intensity of the regularity bands representing the longer helix present in a folded lamellar structure. In other words, it suggests that the long helix structure is more abundantly present than the short helix structure in the aged PP than in the initial PP. By combining the information derived from the SAXS profiles and NIR spectra, the details of the aging-induced variation were clearly determined. Namely, aging causes additional crystallization of the PP by developing more helical structures, which involves an increase in the lamellar thickness as well as a decrease in the amorphous region. The growth of the rigid crystalline phase restricts the elastic deformation in the amorphous structure, which eventually induces the deterioration of PP by making the polymer hard but brittle. Such observation, in turn, implies that retarding or accelerating the crystallized structure of PP substantially works to control the progress of aging.