Enhanced strength of ultrasonically-welded austenitic stainless steels joints by introducing dynamic...

This study investigated the role of interfacial deformability in bond integrity and strength, particularly in the production of robust joints between harder austenitic stainless steels (SS) during ultrasonic welding. The specimen without the interlayer experienced limited strength enhancement owing to internal cracking from continuous sliding at interfacial temperatures below 0.6 times the melting point (T_m), which is attributed to the limited deformability of the austenitic SS. In contrast, introducing Fe and Ni interlayers between the substrates resulted in a notable increase in the interfacial strength, surpassing 2500 N in the peak load within a reduced welding duration. The correlation between the interfacial strength and the peak temperature suggests that a substantial decrease in hardness below 0.4 T_m is sufficient for extensive bond formation. Moreover, dynamic recrystallization (DRX) led to grain refinement in the Fe interlayer owing to shorter weld durations, whereas grain growth was observed in the Ni interlayer due to higher peak temperatures. Both the Fe and Ni interlayers significantly improved the bonding integrity by accommodating plasticity through the above phenomena without severe damage to the substrates, leading to increase of interfacial strength by 24% (2050 N to 2500 N) and reduction of weld duration by 40% (1.5 s in Fe interlayer). In addition, the fracture position after the lap shear test shifted from the edge of the weld area to the SS substrate.