Glass ionomer cement particles pre-reacted with chlorhexidine: Physical/chemical properties and antimicrobial...

Analyze the effects of the functionalization of pre-functionalized GIC particles with chlorhexidine on the physicochemical properties and antimicrobial activity.

Four groups were prepared: (1) GIC (Bioglass R - Biodinamica) - control group; (2) GIC-CHX 1%: Group containing 1% pre-reacted CHX particles; (3) GIC-CHX 2.5%: Group containing 2.5% pre-reacted CHX particles; (4) GIC-CHX 5%: Group containing 5% pre-reacted CHX particles. Hourglass-shaped specimens (10 mm × 2 mm x 1 mm) were fabricated for mechanical tests including cohesive strength (n = 12), modulus of elasticity (n = 12) and microhardness (n = 10). Discs (10 mm × 2 mm) were prepared for the analysis of Ca⁺², PO₄^- and F^- ions release (n = 3), and roughness (n = 12). To evaluate the setting time, a Gilmore needle was used according to ISO 9917-1:2016. Disk-shaped specimens (5 × 1mm) were manufactured and subjected to bacterial activity (n = 9) (Streptococcus mutans ATCC 159).

Modulus, roughness, setting time and ions release (Ca⁺², PO₄^-, and F^-) there were no statistically significant differences among the groups (p > 0.05). The setting time did not change with the incorporation of CHX. The GIC-CHX 2.5% and GIC-CHX 5% groups exhibited superior antibacterial activity compared to the control group and GIC-CHX 1% (p < 0.001). The GIC-CHX 5% group showed the highest microhardness values (p < 0.041), cohesive strength (p < 0.009) when compared to the control group.

The pre-reacted CHX in GICs was able to confer antimicrobial activity, improve cohesive strength, microhardness, and did not impair ion release, setting time, and roughness.