High Magnetic Performance in MnGa Nanocomposite Magnets

In view of their potential applicability in technology fields where magnets are required to operate at higher temperatures, the class of nanocomposite magnets with little or no rare earth (RE) content has been widely researched in the last two decades. Among these nanocomposite magnets, the subclass of magnetic binary systems exhibiting the formation of L1₀ tetragonal phases is the most illustrious. Some of the most interesting systems are represented by the Mn-based alloys, with addition of Al, Bi, Ga, Ge. Such alloys are interesting as they are less costly than RE magnets and they show promising magnetic properties. The paper tackles the case of MnGa binary alloys with various compositions around the Mn₃Ga stoichiometry. Four MnGa magnetic alloys, with Mn content ranging from 70 at% to 75 at% were produced using rapid solidification to form the melt. By combining structural information arising from X-ray diffractometry and transmission electron microscopy with magnetic properties determined by vibrating sample magnetometry, we are able to document the nature and properties of the structural phases formed in the alloys in their as-cast state and upon annealing, the evolution of the phase structure after annealing and its influence on the magnetic behavior of the MnGa alloys. After annealing at 400 °C and 500 °C, MnGa alloys are showing a multiple-phase microstructure, consisting of co-existing crystallites of L1₀ and D0₂₂ tetragonal phase. As a consequence of these structurally and magnetically different phases, co-existing within the microstructure, promising magnetic features are obtained, with both coercive fields and saturation magnetization exceeding values previously reported for both alloys and layers of MnGa.