Radial Inertia Effect of Ultra-Soft Materials from Hopkinson Bar and Solution Methodologies

The split-Hopkinson pressure bar technique is widely used to determine the dynamic mechanical behavior of materials. However, spike-like stress features appear in the initial stress behavior of ultra-soft materials tested with a split-Hopkinson bar. These features are not intrinsic characteristics of the materials. Potential causes were investigated through experiments and numerical simulations. It was found that the spike feature represents derived stress resulting from the radial inertia effect during dynamic loading. In this work, we propose and experimentally verify effective methods to reduce this effect. The influences of density, strain acceleration, ratio between inner and outer diameter, and Poisson's ratio on the radial inertia effect were investigated. The spike stress was found to change linearly with density and strain acceleration but decrease significantly when the inner/outer diameter ratio was below 0.3, after which it remained nearly constant. A parabolic stress distribution was observed along the radial direction due to the Poisson effect, especially when the ratio exceeded 0.3, leading to higher spike stress. Finally, suggestions were proposed as experimental guidance when testing ultra-soft materials.