Impact of Silver Nanoparticle Treatment and Chitosan on Packaging Paper's Barrier Effectiveness

In this study, a comparative analysis of silver nanoparticles treatment and chitosan coating on packaging paper barrier properties was carried out. In order to examine the water, grease, and antibacterial barrier properties of silver nanoparticle-treated and chitosan-coated laboratory-obtained paper samples, a mixture of bleached softwood and hardwood celluloses was used. In order to conduct the comparative analysis SEM, water contact angle, Cobb₆₀, and Kit tests were carried out on a cellulose sample, and four paper samples (three of them treated with silver nanoparticles-1, 2, and 3 mL/20 cm² or chitosan coated-0.5, 1, and 2 g/m²) together with the inhibition activity against nine Gram-positive and Gram-negative bacteria, yeast, and fungal strains. The study found out that increasing the silver nanoparticle treatment and chitosan coating led to improved water resistance, while grease resistance was improved only for chitosan coated paper samples. Additionally, paper treated with 3 mL/20 cm² of silver nanoparticles had the highest antibacterial protection (81.6%) against the Gram-positive bacterium Staphylococcus aureus, followed by Gram-negative Escherichia coli (75.8%). For the rest of the studied microorganisms, the average efficiency of the treated paper was 40.79%. The treatment of the paper with 1 and 2 mL/20 cm² of silver nanoparticles was less effective-27.13 and 39.83%, respectively. The antibacterial protection of 2 g/m² chitosan-coated paper samples was the most effective (average 79%) against the tested bacterial, yeast, and fungal strains. At 1 and 0.5 g/m² chitosan coatings, the efficiency was 72.38% and 54.67%, respectively. Gram-positive bacteria, yeasts, and fungal strains were more sensitive to chitosan supplementation.