Effect of green tea extract antioxidant on dentin shear bond strength and resin-tag penetration depth after non-vital...

Background: 35% Hydrogen peroxide (H ₂O ₂) as an active material for internal bleaching can produce free radicals that can affect resin tag penetration into the dentinal tubules. Application of 10% and 35% green tea (GT) extract as an antioxidant after 2 minutes are expected to remove free radical residues and increase dentin shear bond strength and resin tags penetration depth after non-vital bleaching. Methods: 30 extracted healthy human premolars were cut horizontally 2 mm from the Cemento Enamel Junction margin to the crown part, then cut in a mesio-distal direction into two parts. The specimens were divided into five groups: normal dentin, post bleaching dentin, delayed 2 weeks, 10% GT, and 35% GT group. Non-vital walking bleach with 35% H ₂O ₂ gel was done to all groups except control group. Soon after, 10% and 35% GT extract gel were applied on dentin for 2 minutes, then the specimens were rinsed-off with aquabidest for 2 minutes and dried. All specimens were etched and bonded with an etch-and-rinse adhesive system and filled with resin composite. The shear bond strength assessment was carried out using a Universal Testing Machine (UTM) with a cross-head speed of 0.5 mm/minute. Confocal laser scanning microscopy (CLSM) with a wavelength of 560 nm and a lens magnification of 40x was used to analyze the resin tag penetration. Data were analyzed by one way ANOVA and t-test. Results: There was a significant difference in resin tag penetration depth and shear bond strength between applying 10% and 35% GT extract (p < 0.05). The 35% GT extract group resulted in a significantly longer resin tag penetration than the 10% GT extract group. Conclusions: The application of 35% GT extract is more effective than 10% GT extract as an antioxidant for increasing the shear bond strength of composite resin after internal bleaching.