High-performance Mg-Zn alloy achieved by the ultrafine grain and nanoparticle design

Improving the comprehensive performance of low alloyed Mg is a significant challenge for biomedical applications. This paper developed a high-performance Mg-Zn alloy with uniform ultrafine grains and nano-precipitates through a straightforward, high-temperature reciprocating equal channel angle extrusion (ECAP) process and researched the microstructure, mechanical property, degradation behaviour, and biocompatibility of the developed alloy. Results showed that the lean Mg-2Zn alloy successfully refined grain to about 1 μm and produced plenty of nano-particles with uniform distribution, providing high comprehensive mechanical properties (YS: 235 MPa, UTS: 267 MPa, EL: 15.6 %). Additionally, Zn-riched nano-particles in the matrix could decrease the Zn aggregation at the corrosion layer-matrix interface and form a dense oxide film, achieving a low degradation rate (0.13 mm/year in vivo). Finally, this work realizes the low alloy content, low cost, and good properties of one biodegradable Mg alloy, which will benefit the promotion of future clinical applications.