Biomimetic fiber/hydrogel composite scaffolds based on chitosan hydrogel and surface modified PCL chopped-microfibers

Hydrogel/fiber composites have received wide attention as tissue engineering scaffolds due to the outstanding properties of fibers and hydrogels. In the current research, a hydrogel/fiber composite scaffold was made based on chitosan-modified polycaprolactone (PCL) microfibers and chitosan hydrogel as a binder. The presence of chitosan as a modifier on the surface of fibers and as a binder between fibers can create scaffolds with excellent structural and mechanical properties. To this end, the three-dimensional microfibers were first functionalized with amine groups. Then, the chitosan chains were attached to the fibers by an aldehyde coupling agent and Schiff base reaction. FTIR and Raman spectroscopies corroborated that chitosan was successfully immobilized on PCL fibers. Chitosan-modified fibers were molded with chitosan solutions of various concentrations and the prepared composite scaffolds were stabilized using ionic crosslinking. The obtained composites represented a porous 3D structure with highly interconnected pores. The compressive modulus increased by 19 and 2.7 folds and the tensile modulus was augmented by 28 and 4 folds, in respective dry and swollen states with increasing hydrogel concentration from 0.1 to 1 %. Hydrogel/fiber composites were able to preserve cell viability, and increasing the hydrogel proportion increased adhesion, proliferation and penetration of cells into the scaffold.