Modulation of π-Electron Density in Ultrathin 2D Layers of Graphite Carbon Nitride for Efficient Photocatalytic...

The rational design and synthesis of novel semiconductor nano-/quantum materials have been ambitiously pursued in the field of photocatalysis as the technology is promising and critical for attaining future energy and environmental sustainability. Herein, the integrity of aromatic carbon into graphitic carbon nitride (CN) at the same molecular plane with a few 2D layers is achieved by using modulated precursors of CN, forming carbon regulated ultrathin CN (CUCN) with improved charge transfer kinetics and photocatalytic hydrogen production. The grafted graphite rings adjacent to carbon nitride frameworks induce a significant rearrangement and relocalization of the overall framework, and form conjugated sp² hybridized interfaces and internal electric fields that drive the separation and directional transfer of photogenerated electrons from CN sheets towards intralayer graphite regions, where the photocatalytic hydrogen evolution reaction occurs extensively, yielding largely increased HER rate of 2231.8 µmol g^-1 h^-1 by 8.2 times relative to CN, as well as a remarkable apparent quantum yield of 2.93% under monochromatic light at 420 nm. The high physicochemical stability and low synthesis cost of CUCN make it a potential benchmark photocatalyst that can be readily modified via element doping, heterojunction introduction, defect engineering, and so on, to further enhance its HER performance.