Diversity of short-term DC outcomes in bulk-fill RBCs subjected to a 3 s high-irradiance protocol
Hamad Algamaiah1, Abdulrahman Alshabib1, Muadh Algomaiah2
1Department of Restorative Dental Science, College of Dentistry, King Saud University, P.O. Box 60169, Riyadh 11545, Saudi Arabia.
Objectives:
To determine the short-term (5 min) initial effects of a high-irradiance light-curing (LC) protocol on light transmission (LT%), radiant exposure (RE) and degree of conversion (DC%) of different bulk-fill resin-based composites (RBCs).
Materials And Methods:
Six bulk-fill composites with different viscosities were investigated: OBF (One Bulk Fill, 3 M), EB (Estelite bulkfill,Tokuyama), PFill, PFlow, ECeram and EFlow (PowerFill, Poweflow, Tetric EvoCeram bulkfill, Tetric Evoflow bulkfill, Ivoclar), subjected to different LC protocols: one ultra-high-intensity (3 W/cm2 -3 s via PowerCure LCU) and two conventional (1.2 W/cm2 -10 s and 20 s via PowerCure and Elipar S10 LCUs). Specimens (n = 5) were polymerized within their molds (ϕ5 mm × 4 mm depth) to determine LT% and RE at 4 mm using a MARC-LC spectrometer. For real-time DC% measurements by FTIR, similar molds were utilized. Data were analyzed by one-way ANOVA and Tukey post-hoc tests at 5 % significance.
Results:
Regardless of the applied LC protocols, OBF and low-viscosity RBCs (EB, PFlow and EFlow) had the lowest and highest LT%, RE, DC% and RPmax, respectively. RE results of all RBCs were in the same sequence: Elipar-20 s > PCure-10 s > PCure-3 s. DC% of PFill and PFlow displayed no significant difference between the applied LC protocols (p > 0.05). The polymerization kinetic in all materials was well described by an exponential sum function (r2 varied between 0.85 and 0.98), showing a faster polymerization with the PCure-3 s protocol.
Significance:
The measurement of LT% and DC% at 5 min gave an insight into the developing polymerization process. The initial response of these bulk-fill composite to a high-irradiation protocol varied depending on their composition and viscosity, being faster for low viscosity materials. Nevertheless, even though multiple resin composites are designed to be efficient during photopolymerization, care should be taken when selecting materials/curing protocol.