Green and renewable thermoplastic polyvinyl alcohol/starch blend film fabricated by melt processing

In this study, the PVA/starch blend films were prepared by dry melting method. The microstructure showed that the starch existed in the continuous PVA matrix in granular structure. When the amount of starch was 30 wt%, the tensile strength increased from 12.8 to 14.7 MPa, and the elastic modulus increased from 15.4 to 20.5 MPa, and the water absorption increased by about 2 %. The addition of starch increased the T_max by 8.1-29.64 °C compared to pure PVA. Considering the mechanical, hydrophilic and optical properties of the blend films, PVA/starch at 7:3 was the most promising packaging material. Notably, the blend films exhibit great reusability and renewability. Overall, these findings highlight the potential of PVA/starch blend films as environmentally friendly materials with enhanced properties.