Production of Metal Nanoparticles by Pulsed Laser-ablation in Liquids: A Tool for Studying the Antibacterial Properties of Nanoparticles
Published on: June 2, 2017
The Impact of Silver Nanoparticles' Size on Biofilm Eradication
Ghazal Fakeeha1, Sarah AlHarbi2, Sayed Auda3
1Department of Restorative Dental Sciences, College of Dentistry, King Saud University, Riyadh, Saudi Arabia.
Introduction:
Efficient intracanal disinfection is required for a successful regenerative endodontic treatment. Thus, this study aimed to identify the silver nanoparticles' (NPs) size (AgNPs) with the highest antibiofilm efficacy when mixed with calcium hydroxide [Ca(OH)2] to eradicate an in vitro endodontic biofilm.
Methods:
The various sizes of AgNPs and mixtures were characterized by scanning electron microscopy, transmission electron microscopy, and ultraviolet-visible spectroscopy. A total of 168 dentin root segments were prepared, sterilized, and inoculated for 3 weeks with Actinomyces naeslundii and Fusobacterium nucleatum. Samples were randomly allocated to 4 experimental groups (n = 28/group): 2 nm AgNPs + 35% Ca(OH)2, 5 nm AgNPs + 35% Ca(OH)2, 10 nm AgNPs + 35% Ca(OH)2, and 35% Ca(OH)2 alone. Samples exposed to saline and triple antibiotic paste (TAP) acted as negative and positive control groups, respectively. After 1 and 2 weeks, samples were stained with LIVE/DEAD BacLight dye and examined under a confocal laser scanning microscope to determine the proportion of dead bacteria.
Results:
The characterization procedure revealed a spherical NP's structure with minor aggregations. Except for Ca(OH)2 group, all groups had significantly higher antibiofilm efficacy at 2 weeks. Both the 10 nm mixture (99.5%) and TAP (99.2%) exhibited the highest antibiofilm efficacy at 2 weeks and were not significantly different from one another (P > .05). No significant difference was noted between the 2 and 5 nm mixtures at 1 week (81% and 84%) and 2 weeks (89% and 91%).
Conclusion:
The 10 nm AgNPs (0.02%) + 35% Ca(OH)2 mixture exhibited the highest antibiofilm efficacy at 2 weeks compared to all other mixtures at both observation periods. Interestingly, the 10 nm mixture performed similarly to TAP at 2 weeks. Excluding Ca(OH)2 group, longer application significantly improved the antibiofilm efficacy of all tested medicaments.
Clinical Relevance:
The 10 nm AgNPs + 35% Ca(OH)2 mixture revealed promising results as an intracanal medicament in the regenerative endodontic treatment protocol.
More Related Videos
11:19Synthesis of Multi-walled Carbon Nanotubes Modified with Silver Nanoparticles and Evaluation of Their Antibacterial Activities and Cytotoxic Properties
Published on: May 10, 2018
11:52Evaluation of Antimicrobial Activities of Nanoparticles and Nanostructured Surfaces In Vitro
Published on: April 21, 2023
Related Concept Videos
01:23Factors Affecting Dissolution: Particle Size and Effective Surface Area
01:29Biofilms
01:28Antimicrobial Effectiveness