Study on the Storage Stability and Rheological Property of Bio-Oil/Lignin Composite-Modified Asphalt

The objective of this study is to investigate the storage stability and rheological property of bio-oil/lignin composite-modified asphalt. The composite-modified asphalt with different proportions of bio-oil was prepared and cured at 105 °C, 135 °C, and 165 °C for 24 h and 48 h. The storage stability of the composite-modified asphalt was evaluated based on the softening point difference, the storage stability index derived from rotational viscosity, the segregation rate based on temperature sweep, and the non-recoverable creep compliance measured through the Multiple Stress Creep Recovery test. The storage stability of bio-oil/lignin composite-modified asphalt was evaluated through testing and analysis of its infrared spectroscopy and scanning electron microscopy before and after thermal storage. The research results indicate that the maximum difference in softening point is 0.9 °C, and the calculated storage stability index is generally below 0.1. The maximum value of the segregation rate is 0.43, indicating excellent storage stability of the bio-oil/lignin composite-modified asphalt. According to the results from infrared spectroscopy, no chemical reactions occurred during the storage process of the composite-modified asphalt. The scanning electron microscope confirmed that the samples became more stable after 48 h of storage.