Life-Cycle Assessment and Environmental Costs of Cement-Based Materials Manufactured with Mixed Recycled Aggregate...

The development of new building elements, such as concrete and mortar with sustainable materials, which produce a lower carbon footprint, is an achievable milestone in the short term. The need to reduce the environmental impact of the production of cement-based materials is of vital importance. This work focuses on the evaluation of the life-cycle assessment, production costs, mechanical performance, and durability of three mortars and three concrete mixtures in which mixed recycled aggregates (MRAs) and biomass bottom ash from olive waste (oBBA) were included to replace cement and aggregates. Powdered MRA and oBBA were also applied as complementary cementitious materials with a reduced environmental footprint. Chemical and physical tests were performed on the materials, and mechanical performance properties, life-cycle assessment, and life-cycle cost analysis were applied to demonstrate the technical and environmental benefits of using these materials in mortar and concrete mixtures. This research showed that the application of MRA and oBBA produced a small reduction in mechanical strength but a significant benefit in terms of life-cycle population and environmental costs. The results demonstrated that finding long-term mechanical strength decreases between 2.7% and 14% for mortar mixes and between 1.7% and 10.4% for concrete mixes. Although there were small reductions in mechanical performance, the savings in environmental and monetary terms make the feasibility of manufacturing these cement-based materials feasible and interesting for both society and the business world. CO₂ emissions are reduced by 25% for mortar mixes and 12% for concrete mixes with recycled materials, and it is possible to reduce the cost per cubic meter of mortar production by 20%, and the savings in the cost of production of a cubic meter of concrete is 13.8%.