Development of a Superhydrophobic Protection Mechanism and Coating Materials for Cement Concrete Surfaces

In order to further enhance the erosion resistance of cement concrete pavement materials, this study constructed an apparent rough hydrophobic structure layer by spraying a micro-nano substrate coating on the surface layer of the cement concrete pavement. This was followed by a secondary spray of a hydroxy-silicone oil-modified epoxy resin and a low surface energy-modified substance paste, which combine to form a superhydrophobic coating. The hydrophobic mechanism of the coating was then analysed. Firstly, the effects of different types and ratios of micro-nano substrates on the apparent morphology and hydrophobic performance of the rough structure layer were explored through contact angle testing and scanning electron microscopy (SEM). Subsequently, Fourier transform infrared spectroscopy and permeation gel chromatography were employed to ascertain the optimal modification ratio, temperature, and reaction mechanism of hydroxy-silicone oil with E51 type epoxy resin. Additionally, the mechanical properties of the modified epoxy resin-low surface energy-modified substance paste were evaluated through tensile tests. Finally, the erosion resistance of the superhydrophobic coating was tested under a range of conditions, including acidic, alkaline, de-icer, UV ageing, freeze-thaw cycles and wet wheel wear. The results demonstrate that relying solely on the rough structure of the concrete surface makes it challenging to achieve superhydrophobic performance. A rough structure layer constructed with diamond micropowder and hydrophobic nano-silica is less prone to cracking and can form more "air chamber" structures on the surface, with better wear resistance and hydrophobic performance. The ring-opening reaction products that occur during the preparation of modified epoxy resin will severely affect its mechanical strength after curing. Controlling the reaction temperature and reactant ratio can effectively push the modification reaction of epoxy resin through dehydration condensation, which produces more grafted polymer. It is noteworthy that the grafted polymer content is positively correlated with the hydrophobicity of the modified epoxy resin. The superhydrophobic coating exhibited enhanced erosion resistance (based on hydrochloric acid), UV ageing resistance, abrasion resistance, and freeze-thaw damage resistance to de-icers by 19.41%, 18.36%, 43.17% and 87.47%, respectively, in comparison to the conventional silane-based surface treatment.