Lifecycle Assessment and Multi-Parameter Optimization of Lightweight Cement Mortar with Nano Additives

With the growing global concerns regarding sustainable development in the building and construction industries, concentration only on the engineering properties of building materials can no longer meet the requirements. Although some studies have been implemented based on the lifecycle assessment of lightweight cement-based materials, very few attempts have been made pertaining to multi-criteria optimization, especially when fly ash cenospheres are used as lightweight aggregates and nano additives are incorporated as modifying admixtures. This investigation utilized cenospheres as fine aggregates to produce green, sustainable, lightweight cement mortar. Multi-walled carbon nanotubes at 0.05, 0.15, and 0.45% were binarily added, together with 0.2, 0.6, and 1.0% of nano silica to improve the mechanical performance. Strength tests were conducted to measure the flexural and compressive behaviors, combined with a cradle-to-gate lifecycle assessment and direct cost analysis to assess the environmental and economic viability. Integrated indexes and the TOPSIS method were adopted to systematically evaluate the mortar mixes and determine the optimal mix. The outcomes show that nano additives worked synergically to enhance the mechanical properties of the mortars. The utilization of cenospheres effectively reduced environmental impacts and improved economic feasibility. Nano additives significantly affected the sustainability and economic viability; in particular, the utilization of multi-walled carbon nanotubes increased the material costs. To minimize the impact of the price of multi-walled carbon nanotubes, it is proposed to binarily use less expensive nano silica. In the multi-parameter optimization, the mix with 0.05% multi-walled carbon nanotubes and 0.02% nano silica was recommended to be the optimal mix.