Microhoneycomb Monoliths Prepared by the Unidirectional Freeze-drying of Cellulose Nanofiber Based Sols: Method and Extensions
Published on: May 24, 2018
Preparation of Hierarchical Porous Monoliths With High Surface Areas by a Solvent Knitting Strategy
Zicheng Zhong1, Xiaojie Peng1, Hui Gao1
1Key Laboratory of Material Chemistry for Energy Conversion and Storage, Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan, 430074, China.
Abstract:
Hierarchical porous hypercrosslinked monoliths (PolyHIPE-HCP) with ultrahigh specific surface areas are prepared via a solvent knitting strategy. Compared to previous work, the solvent knitting strategy is carried out in a relatively low air-controlled atmosphere with gradient heating starting from low temperature while using DCM (Dichloromethane) as both a solvent and a cross-linker, allowing for a slow and controlled cross-linking process, thereby achieving a BET surface area ranging from 514 to 728 m2 g-1. Scanning electron microscopy (SEM) shows that the knitting process does not affect the presence of macroporous structure in the PolyHIPE. With the introduction of mesopores and micropores, these hierarchical porous monoliths exhibit significant potential for applications in gas adsorption and water treatment. Hence, a universal, simple and low-cost method to synthesize polymeric monoliths with hierarchically porous structure and higher surface area is proposed, which has fascinating prospects in industrialization.