Developing flame retardant, smoke suppression and self-healing polyvinyl alcohol composites by dynamic reversible...

With the increasing threat of white pollution to the public health and ecosystem, functional materials driven by green and sustainable biological macromolecule are attracting considerable attention. Inspired by the double-helix structure of DNA, a P-B-N ternary synergistic chitosan-based macromolecule (PBCS) was constructed to prepare flame retardant, smoke suppression and self-healing polyvinyl alcohol composite (PVA@PBCS) via dynamic reversible interactions. The limiting oxygen index value of PVA@PBCS increased from 19.6 % to 28.7 %, whereas the peak heat release rate and total heat release decreased by 47.04 % and 43.37 %, respectively. Besides, the peak smoke production rate and total smoke production of PVA@PBCS also decreased by 45.31 % and 54.98 %. With the presence of borate ester-based covalent and multiple hydrogen bonds, the tensile strength and elongation at break of PVA@PBCS increased by 19.50 % and 16.85 % compared to the control sample, and the healing efficiency for tensile strength and elongation at break was as high as 93.86 % and 90.57 %, respectively. This work developed an eco-friendly and effective scenario for fabricating flame retardant and smoke suppression PVA materials, stimulating the substantial potential of chitosan-based biomacromolecule and dynamic reversible cross-linked tactics in self-healing field.