High-Entropy Ag-Ru-Based Electrocatalysts with Dual-Active-Center for Highly Stable Ultra-Low-Temperature Zinc-Air...

The development of advanced bifunctional catalysts for oxygen evolution reaction (OER) and oxygen reduction reaction (ORR) is significant for rechargeable zinc-air batteries (ZABs). Herein, a unique dual active center alloying strategy is proposed to achieve the efficient bifunctional oxygen catalysis, and the high entropy effect is further exploited to modulate the structure and performance of the catalysts. The MOF-assisted pyrolysis-replacement-alloying method was employed to construct the CoCuFeAgRu high-entropy alloy (HEA), which are uniformly anchored in porous nitrogen-doped carbon nanosheets. Notably, the obtained HEA catalyst exhibits excellent catalytic performance for both ORR and OER, and a peak power density of 136. 53 mW cm^-2 and an energy density of 987.9 mAh g_Zn ^-1, surpassing the most of the previously reported bifunctional oxygen electrocatalysts. Moreover, the assembled flexible rechargeable ZAB enables excellent performance even at the ultralow temperature of -40 °C, with an energy density of 601.6 mAh g_Zn ^-1 and remarkable cycling stability up to 1,650 hours. Combined experimental and theoretical calculation results reveal that the excellent bifunctional catalytic activity of the HEA catalyst originated from the synergistic effect of the Ag and Ru dual active centers, and the optimization of the electronic structure by alloying effect.