Can wheel polishers improve surface properties and color stability of monochromatic resin composites?
Lezize Sebnem Turkun1, Cankut Canevi1, Alperen Degirmenci2
1School of Dentistry, Department of Restorative Dentistry, Ege University, Izmir, 35040, Turkey.
Background:
To overcome the color layering procedure, monochromatic resin composites have been introduced. However, little is known about their polishability, gloss and color stability. This study aimed to investigate the surface roughness, gloss, and color change of monochromatic resin composites polished with wheel systems after being immersed in coffee.
Materials And Methods:
Omnichroma, Zenchroma, Essentia Universal, Charisma Diamond One and NeoSpectra ST were used to obtain 120-disc samples of 8 × 2 mm. Only one side of the sample was polished with Twist Dia (TWD) or Nova Twist (NOV). The samples were examined for surface roughness, gloss, and color (ΔE and ΔE00) before and after 7 days of immersion in coffee and subsequent repolishing. The discs were examined via SEM. Surface roughness and gloss values were analyzed using ANOVA, Tukey and Pearson correlation tests. ΔE and ΔE00 values were evaluated using T tests, multivariate ANOVA, and Dunnett's post-hoc tests.
Results:
For TWD groups, the smoothest material was Omnichroma (p < 0.05), while for NOV groups, it was Omnichroma and Zenchroma. Omnichroma was the glossiest, while Charisma Diamond One was the least glossy. In TWD groups, Charisma Diamond One and Essentia Universal were the most discolored, while Zenchroma and Omnichroma were the least. For NOV groups, Essentia Universal and Charisma Diamond One were the most discolored, while NeoSpectra ST, Omnichroma and Zenchroma were the least. After repolishing, Charisma Diamond One did not reach the level of ΔE < 2, while the other groups showed values below. Color evaluation with the CIELab and CIEDE2000 systems revealed similar results for the TWD groups after post-staining.
Conclusions:
Smooth and glossy surfaces could be achieved with the wheel system regardless of the composite resin. Repolishing after discoloration ensures that the color recovery is below the acceptable limit. Color evaluations with CIELab and CIEDE2000 yielded similar results.