Controlled chemical transformation of lignin by nitric acid treatment and carbonization

This study focuses on understanding the chemical reactions and results of Kraft lignin transformation through nitric acid treatment and subsequent carbonization. With its rich carbon content, lignin stands out as a promising candidate for the manufacturing of high-value carbon materials. The lignin underwent effective nitration, depolymerization, and oxidation under ambient conditions and at 40 °C, while a slight increase in reaction temperature significantly reduced the reaction time. The molecular weight M_w was effectively reduced from 4371 g/mol to 767 g/mol. The acid-treated lignin samples with incorporated nitro groups were further carbonized to create nitrogen-doped carbon structures. The resulting materials show stable nitrogen content (about at 5 wt%) even after carbonization due to the transformation of nitro groups into thermally stable pyridinic moieties, thereby exhibiting enhanced electrocatalytic properties compared to nitrogen-free carbon materials derived from Kraft lignin. The nitric acid-assisted treatment of lignin obviates the need for catalysts, and additional extraction or purification steps for preparing bio-derived carbon precursors, rendering it facile, fast, and cost-efficient.