Stable Field Emission from Single-Crystalline Zirconium Carbide Nanowires

The <100> oriented single-crystalline Zirconium Carbide (ZrC) nanowires were controllably synthesized on a graphite substrate by chemical vapor deposition (CVD) with optimized growth parameters involving Zirconium tetrachloride (ZrCl₄), flow of methane (CH₄), and growth temperature. The length of nanowires is above 10 µm while the diameter is smaller than 100 nm. A single ZrC nanowire was picked up and fixed on a tungsten tip for field emission measurement. After surface pretreatments, a sharpened and cleaned ZrC nanowire emitter showed a high emission current density of 1.1 × 10¹⁰ A m^-2 at a low turn-on voltage of 440 V. The field emission is stable for 150 min with a fluctuation of 1.77%. This work provides an effective method for synthesizing and stabilizing single-crystalline ZrC nanowire emitters as an electron source for electron-beam applications.