Highly Tensile Strained Cu(100) Surfaces by Epitaxial Grown Hexagonal Boron Nitride for CO2 Electroreduction to C2+
Qiuwen Liu1, Yao Tan1, Qin Chen1
1Hunan Joint International Research Center for Carbon Dioxide Resource Utilization, School of Physics, Central South University, Changsha 410083, Hunan, P. R. China.
Abstract:
Copper (Cu) has been considered as the most promising catalyst for the electrochemical conversion of CO2 to multicarbon (C2+) products. However, insufficient coverage of the *CO intermediate on the C2+ formation Cu(100) facet largely hinders the C-C coupling process and thus the C2+ conversion efficiency. Herein, we developed an epitaxial growth strategy to generate highly tensile-strained Cu(100) facets via the epitaxial growth of hexagonal boron nitride (hBN) on Cu(100) facets to promote *CO coverage for efficient CO2 to C2+ conversion. The highest ∼6% tensile strain on the Cu(100) facets was obtained by lattice mismatch between the Cu(100) and hBN(002) facets. Theory calculations indicated that tensile-strained Cu(100) facets deliver a notable d-band center upshift to enhance *CO adsorption. As a result, the obtained highly tensile-strained Cu(100) facets enabled an 8-fold improvement of *CO coverage and thus a 83.4% C2+ Faradaic efficiency at 1.2 A cm-2 in strongly acidic electrolyte (pH = 1).