Fiber post cemented using different adhesive strategies to root canal dentin obturated with calcium silicate-based...

Calcium silicate-based sealer has favorable properties for root canal filling, including hydroxyapatite formation during the setting process. However, this process can cause difficulty during post space preparation when the sealer is set. Additionally, the remaining sealer could interfere with the bond strength of fiber post to root canal dentin. The different adhesive strategies and fiber post cementation time may affect the bond strength of the fiber post. Thus, the objective of this study was to evaluate the effect of etching modes of Scotchbond™ Universal Plus adhesive and post cementation time on the push-out bond strength of a fiber post cemented in root canals obturated with calcium silicate-based sealer.

Fifty-four teeth were randomly allocated to 6 groups (n = 9) based on etching modes: self-etch (SE) or etch-and-rinse (ER); post space preparation and cementation time: immediate (Im) or 7-day delayed (De): Im-Im, Im-De, and De-De. The root canals were obturated with calcium silicate-based sealer and the post space preparation was performed. The fiber post was cemented using RelyX™ Universal resin cement according to each group's design. For the push-out bond strength test, 1-mm slices of the coronal, middle, and apical regions were tested using a universal testing machine. The failure mode analysis was determined using a stereomicroscope. The data was analyzed with three-way analysis of variance.

No negative effects of etching modes, post space preparation or cementation time on push-out bond strength were detected (p > 0.05). Additionally, the root canal region also did not significantly affect the bond strength (p > 0.05).

No significant differences were observed between the etching modes, post space preparation and cementation time and among root canal regions.

The different etching modes of adhesive and post cementation time did not affect the bond strength of fiber post in calcium silicate filled-root canal.