Locally Injectable Chitosan/β-Glycerophosphate Hydrogel Doped with Triptolide-Human Serum Albumin Nanoparticles for...

Rheumatoid arthritis (RA) tends to occur in symmetrical joints and is always accompanied by synovial hyperplasia and cartilage damage. Triptolide (TP), an extract from Tripterygium, has anti-inflammatory and immunomodulatory properties and could be used in the treatment of RA. However, its poor water solubility and the multi-system lesions caused by the use of this substance limit its clinical application. Therefore, it would be of great significance to assemble a composite nanoparticle hydrogel and apply it to a collagen-induced arthritis (CIA) mouse model to investigate the therapeutic effect and biosafety of this compound.

TP@HSA nanoparticles (TP@HSA NPs) were fabricated with a self-assembly method; a thermosensitive hydrogel loaded with the TP@HSA NPs (TP@HSA NP hydrogel) was prepared by using chitosan and beta- glycerophosphate (β-GP) and was then intra-articularly injected into CIA mice. The changes in joint swelling were measured with a digital caliper, and inflammation and cartilage damage were evaluated by using hematoxylin and eosin (H&E) and safranin O-fast green (SO&FG) staining, respectively.

TP@HSA NPs with an average diameter of 112 ± 2 nm were successfully assembled, and their encapsulation efficiency and drug loading efficiency were 47.6 ± 1.5% and 10.6 ± 3.3%, respectively. The TP@HSA NP hydrogel had a gelation temperature of 30.5 ± 0.2 °C, which allows for its injection at low temperatures and its sol-gel transformation under physiological conditions within 2 min, making it a suitable drug depot. The TP@HSA NP hydrogel was intra-articularly injected into CIA mice; it released TP locally and exerted anti-inflammatory and immunomodulatory effects, alleviating synovial inflammation and cartilage damage effectively.

We successfully fabricated a TP@HSA NP-loaded thermosensitive hydrogel with good biosafety, which can release TP slowly for the treatment of RA. Our study provides a basis for the development of TP-based innovative preparations and has good application prospects.