Study on Acoustic Emission Characteristics and Damage Mechanism of Wind Turbine Blade Main Spar with Different...

This paper aimed to understand the AE signal characteristics and damage mechanism of wind turbine blade main spar materials with different defects during the damage evolution process. According to the typical delamination and wrinkle defects in wind turbine blades, the GFRP composite with defects is artificially prefabricated. Through acoustic emission experiments, the mechanical properties and acoustic emission characteristic trends of wind turbine blade main spar composites with different defects under tensile loading conditions were analyzed, and the damage evolution mechanism of different defects was explained according to the microscopic results. The results show that the existence of artificial defects will not only affect the mechanical properties of composite materials but also affect the damage evolution process of the materials. The size and location of delamination defects and the different aspect ratio of the wrinkle defects have a certain influence on the damage mechanism of the material. K-means cluster analysis of AE parameters identified the damage models of GFRP composites. The types of damage modes of delamination defects and wrinkle defects are the same, and the range of characteristic frequency is roughly the same. This study has important reference significance for structural damage monitoring and damage evolution research of wind turbine blade composites.