Broad Range Tuning of InAs Quantum Dot Emission for Nanophotonic Devices in the Telecommunication Bands

InAs semiconductor quantum dots (QDs) emitting in the near-infrared are promising platforms for on-demand single-photon sources and spin-photon interfaces. However, the realization of quantum-photonic nanodevices emitting in the telecom windows with similar performance remains an open challenge. In particular, nanophotonic devices incorporating quantum light emitting diodes in the telecom C-band based on GaAs substrates are still lacking due to the relaxation of the lattice constant along the InGaAs graded layer which makes the implementation of electrically contacted devices challenging. Here, we report an optimized heterostructure design for QDs emitting in the telecom O- and C-bands grown by means of molecular beam epitaxy. The InAs QDs are embedded in mostly relaxed InGaAs matrices with fixed indium content grown on top of compositionally graded InGaAs buffers. Reciprocal space maps of the indium profiles and optical absorption spectra are used to optimize In_0.22Ga_0.78As and In_0.30Ga_0.70As matrices, accounting for the chosen indium grading profile. This approach results in a tunable QD photoluminescence (PL) emission from 1200 up to 1600 nm. Power and polarization dependent micro-PL measurements performed at 4 K reveal exciton-biexciton complexes from quantum dots emitting in the telecom O- and C-bands. The presented study establishes a flexible platform that can be an essential component for advanced photonic devices based on InAs/GaAs that serve as building blocks for future quantum networks.