Investigation of Damping Properties of Natural Fiber-Reinforced Composites at Various Impact Energy Levels

Natural fiber-reinforced composites are composite materials composed of natural fibers, such as plant fibers and synthetic biopolymers. These environmentally friendly composites are biodegradable, renewable, cheap, lightweight, and low-density, attracting attention as eco-friendly alternatives to synthetic fiber-reinforced composites. In this study, natural fiber-reinforced polymer foam core layered composites were produced for the automotive industry. Fabrics woven from goat wool were used as the natural fiber. Polymer foam with expanded polystyrene (EPS) and extruded polystyrene (XPS) structures was used as the core material. During production, fibers were bonded to the upper and lower layers of the core structures using resin. The hand lay-up method was used in production. After resin application, the samples were cured under a heated press for 2 h. After the production was completed, the material was cut according to the standards (10-20-30 Joule), and impact and bending tests were conducted at three different energy levels. The experiments revealed that at 10 J, the material exhibited rebound; at 20 J, it showed resistance to stabbing; and at 30 J, it experienced penetration. While EPS foam demonstrated higher impact resistance in the 10 J test, it was found that XPS foam exhibited better impact resistance and absorption capabilities in the 20 J and 30 J tests. Due to the open and semi-closed cell structure of EPS foams and the closed cell structure of XPS foams, it has been concluded that XPS foams exhibit higher impact resistance and better energy absorption properties.