Quality Investigation of Pultruded Carbon Fiber Panels Subjected to Four-Point Flexure via Fiber Optic Sensing

Pultruded carbon fiber-reinforced composites are attractive to the wind energy industry due to the rapid production of highly aligned unidirectional composites with enhanced fiber volume fractions and increased specific strength and stiffness. However, high volume carbon fiber manufacturing remains cost-prohibitive. This study investigates the feasibility of a pultruded low-cost textile carbon fiber-reinforced epoxy composite as a promising material in spar cap production was undertaken based on mechanical response to four-point flexure loading. As spar caps are primarily subjected to flexural loading, large-span four-point flexure was considered, and coupon testing was restricted to tensile modulus and compression strength assessment. High-resolution spatial fiber optic strain sensing was utilized to determine spatial strain distribution during four-point flexure, revealing consistent strain along the length of the part and proved to be an excellent option for process manufacturing quality examination. Additionally, holes with diameters of 2.49 mm, 5.08 mm, and 1.93 mm were drilled through the thickness of full-width parts to determine the feasibility of structural health monitoring of pultruding parts internal to wind blades via fiber optic strain sensing.